To analyze the biodegradability of

To analyze the biodegradability of each bioplastic clearly, the powdered bioplastics were added in soil and the
rate of decrease in soil TC was measured after 28 days. The degradation ratios of PBS-starch, PBS, and PLA after
28 days were 24.4%, 16.8%, and 13.8%, respectively. These bioplastics were degraded faster than the commercial
bioplastics (Figure 3). The enhancement of biodegradability of powdered bioplastics in the soil seemed
to be caused by increase in the surface area. The tendency of the relative biodegradabilities of each powderedbioplastics
was similar to those of the commercial bioplastics.

Результаты (русский) 1:

Чтобы проанализировать способность к биологическому разложению каждого биопластмасс ясно, пудры биопластиков были добавлены в почве иснижение в почве TC была измерена после 28 дней. Показатели деградации PBS-крахмал, PBS и PLA после28 дней с 24,4%, 16,8%, 13,8%, соответственно. Эти биопластиков были деградируют быстрее, чем коммерческиебиополимеров (рис. 3). Казалось, повышение к биологическому разложению биопластиков пудры в почвечтобы быть вызвано увеличением площади поверхности. Тенденция относительной biodegradabilities каждый powderedbioplasticsбыл похож на тех коммерческих биопластиков.

Результаты (русский) 2:

Для анализа биоразлагаемости каждого ясно, были добавлены порошкообразные биопластика в почве биопластика и
темп снижения почвы TC измеряли через 28 дней. Коэффициенты деструкции PBS-крахмала, PBS, и ПЛА после
28 дней были 24,4%, 16,8%, и 13,8%, соответственно. Эти биопластика деградировали быстрее , чем коммерческие
биопластика (рисунок 3). Усиление способности к биологическому разложению порошкообразных биопластика в почве , казалось
, вызвано увеличением площади поверхности. Тенденция относительных биоразлагаемостей каждого из них powderedbioplastics
был похож на тех коммерческих биопластика.