Silicate industry is the industry p

Silicate industry is the industry processing the natural compounds of silicon. *It embraces the production of cement, glass, and ceramics.

The production of ceramic goods is based on the property of clay when mixed with water to form putty, from which various articles can easily be moulded. When these are dried and then for easily moulding baked, that is, ignited at a high temperature, they become hard and retain their shape, no longer being softened by water.

In this way clay, mixed water and sand is moulded into bricks, which are then dried and baked. The materials used to make silicate bricks are white sand and slaked lime.

Cement Production. Cement is made from limestone and clay, or from their natural mixture, marls. The materials roasted in cylindrical rotary kilns are charged into a slowly rotating kiln at its upper end and travel, mixing continuously, towards the lower end, while a current of hot gases, the products of the burning of fuel, flows in the opposite direction. During the period of their movement through the kiln the clay and the limestone react chemically, and the material emerging from the kiln in lumps of a caked mass is cement, which is then grounded.

When cement is mixed with water, it forms mortar, which hard­ens, binding various objects, such as bricks or stones, very firmly. It is for this reason that cement is used widely as a binding materials in large-scale construction, including underwater construction.

Cement is often mixed with sand or gravel, in which case we get concrete. Concrete has roughly the same coefficient of thermal ex­pansion as iron.

Glass Production. The initial materials for the production of or­dinary glass are mainly soda, limestone, and sand. A mixture of these substances is heated in a bath-shaped furnace.

When it cools, the liquid mass of glass *does not become hard at once2. At first it becomes viscous and readily assumes any shape. This property of glass is used in making various articles out of it. Definite portions of the cooling semiliquid mass are taken from the bath, and these are blown or pressed to make various glassware. By machine methods glass sheets, tubes, etc., can be drawn continuous­ly from the molten mass.



Sand is the chief material used as a fine aggregate. It is required in mortar or concrete for economy and to prevent the excessive crack­ing. Mortar made without sand would be expensive.

The word "sand" is applied to any finely divided material which will not injuriously affect the cement or lime and * which is not sub­ject to disintegration or decay. Sand is almost the only material which is sufficiently cheap and which can fulfil these requirements.

A mixture of coarse and fine grains is very satisfactory, as it makes a denser and stronger concrete with a less amount of cement than when only fine-grained sand is used.

The following sands are used for mortars: pit or quarry sand, river sand and sea sand.

Lime is a calcium oxide. It is used in great quantities for mortar and plaster. Lime (quicklime) is a white solid that reacts violently with water to form calcium hydroxide. It is made by heating lime­stone in a special kind of furnace called a "kiln". Lime must be stored in a dry place, otherwise it will absorb moisture.

Limes may be divided into three distinct classes:

1. Rich limes that contain not more than 6 percent of impurities, slake very rapidly, and are entirely dependent *on external agents for setting power4. These are widely used for interior plasterer's works.

2. Poor limes that contain from 15 percent to 30 percent of use­less impurities and possess the general properties of rich limes, only to a lesser degree.

3. Hydraulic limes that contain certain proportions of impurities, which when calcinated, combine with the lime and endow it with the valuable property of setting under water or without external agents.

Lime is a basic building material extensively used all over the world, but it was not until the later years of the 19th century that a greater appreciation of the fuel-burning problems involved became apparent. Until this time the requirement for lime was largely agri­cultural and it was produced by farmers or by small builders who used it for making mortar and plaster.

As industrial requirements increased "running" kilns were devel­oped. These were lined with firebrick and charged at regular inter­vals with stone and fuel.

Around the world there are many different types of kilns and variations in lime-burning practice.

Результаты (русский) 1:

Силикатная промышленность является отраслью, обработки природных соединений кремния. * Она охватывает производство цемента, стекла и керамики.Производство керамических изделий основан на свойства глины при смешивании с водой форму шпаклевки, из которого легко могут быть формованные различных статей. Когда они сушатся и затем для легко литья, запеченные, то есть, воспламеняется при высокой температуре, они становятся твердыми и сохраняют свою форму, больше не смягченной водой.Таким образом формируется глины, смешанной воды и песка в кирпичи, которые затем сушат и запеченные. Материалы, используемые для силикатного кирпича, белый песок и Известь гашеная.Производство цемента. Цемент производится из известняка и глины, или от их природной смеси, мергели. Материалы, жареные в цилиндрических вращающихся печах начисляются в медленно вращающейся печи на верхнем конце и путешествия, смешивая непрерывно, в конце нижней, а ток горячих газов, продукты горения топлива, течет в обратном направлении. В период их перемещения через печь глины и известняка реагируют химически, и материал, выходящих из печи в куски затвердевшей массы цемента, который затем обоснована.Когда цемент смешивают с водой, образует раствор, который затвердевает, привязка различных объектов, таких как кирпичи или камни, очень прочно. Именно по этой причине, что цемент используется широко, как Вяжущие материалы в масштабное строительство, включая подводные конструкции.Цемент часто смешивают с песком или гравием, в этом случае мы получаем бетона. Бетон имеет примерно тот же коэффициент теплового расширения, как железо.Производство стекла. Исходные материалы для производства обычного стекла в основном соды, известняка и песка. Смесь этих веществ нагревается в печи, Ванна образный.Когда он остынет, жидкой массы стекла * не становится трудно на once2. Сначала он становится вязким и легко принимает любую форму. Это свойство стекла используется в изготовления различных изделий из него. Определенные части массы охлаждения полужидкий взяты из ванны, и эти ветром или вынуждены сделать различные стекла. Машины методы стекла листы, трубы и т.д., можно извлечь непрерывно из расплавленной массы.Песок – главный материал, используемый как прекрасный агрегат. Это требуется в раствора или бетона для экономики и для предотвращения чрезмерного трещин. Раствор, без песка будет дорого.Слово «песка» применяется к любому мелко разделить материал, который не повлияет, хищнически цемента или извести и * которая не подлежит дезинтеграции и распада. Песок является практически единственным материалом, который является достаточно дешевой и который может выполнить эти требования.Смесь зерен грубой и тонкой является весьма удовлетворительным, как это делает плотнее и сильнее бетона с меньшим количеством цемента чем когда используется только мелкозернистый песок.Следующие пески используются для строительных смесей: яма или карьер песка, речной песок и море песка.Lime is a calcium oxide. It is used in great quantities for mortar and plaster. Lime (quicklime) is a white solid that reacts violently with water to form calcium hydroxide. It is made by heating lime­stone in a special kind of furnace called a "kiln". Lime must be stored in a dry place, otherwise it will absorb moisture.Limes may be divided into three distinct classes:1. Rich limes that contain not more than 6 percent of impurities, slake very rapidly, and are entirely dependent *on external agents for setting power4. These are widely used for interior plasterer's works.2. Poor limes that contain from 15 percent to 30 percent of use­less impurities and possess the general properties of rich limes, only to a lesser degree.3. Hydraulic limes that contain certain proportions of impurities, which when calcinated, combine with the lime and endow it with the valuable property of setting under water or without external agents.Lime is a basic building material extensively used all over the world, but it was not until the later years of the 19th century that a greater appreciation of the fuel-burning problems involved became apparent. Until this time the requirement for lime was largely agri­cultural and it was produced by farmers or by small builders who used it for making mortar and plaster.As industrial requirements increased "running" kilns were devel­oped. These were lined with firebrick and charged at regular inter­vals with stone and fuel.В мире существует много различных типов печей и вариации в практике сжигания извести.

Результаты (русский) 2:

Силикатная промышленность промышленность обработки природных соединений кремния. * Оно охватывает производство цемента, стекла, и керамики. Производство керамических изделий основан на свойстве глины при смешивании с водой с образованием замазки, из которого различные статьи могут быть легко формуется. Когда они сушат, а затем в течение легко формования запеченные, то есть происходить при высокой температуре, они становятся твердыми и сохраняют свою форму, больше не размягчается водой. Таким путем глины, смешанной воды и песка формуют кирпичи, которые затем сушат и спекают. Материалы, используемые для изготовления силикатного кирпича являются белый песок и гашеная известь. Производство цемента. Цемент производится из известняка и глины или из их смеси, природного мергелей. Материалы, жареные в цилиндрических вращающихся печах загружают в медленно вращающейся печи на своем верхнем конце и путешествий, смешивая непрерывно, к нижнему концу, в то время как ток горячих газов, продуктов сжигания топлива, течет в противоположном направлении. В период их движения через печь глина и известняк вступают в химическую реакцию, и материал, выходящий из печи в кусках в затвердевшей массы цемента, который затем заземлен. При цемент смешивали с водой, он образует раствор, который затвердевает, связывая различные объекты, такие как кирпич или камни, очень твердо. Именно по этой причине, что цемент широко используется в качестве вяжущих материалов в масштабное строительство, в том числе подводного строительства. Цемент часто смешивают с песком или гравием, и в этом случае мы получаем бетон. Бетон имеет примерно такой же коэффициент теплового расширения, как железо. Производство стекла. Исходными материалами для производства обычного стекла, в основном, сода, известняк, и песок. Смесь из этих веществ нагревают в ванне в форме печи. При охлаждении жидкость масса стекла * не станет трудно в once2. Сначала она становится вязкой и легко принимает любую форму. Это свойство стекла используется в изготовлении различных изделий из нее. Определенные участки охлаждения полужидкой массы взяты из ванны, и они взорвали или нажатии сделать различные изделия из стекла. Машиной методы стеклянных листов, труб и т.д., могут быть сделаны непрерывно с расплавленной массы. Песок главный материал, используемый в качестве мелкого заполнителя. Это требуется в раствор или бетон для экономики и для предотвращения чрезмерного растрескивания. Раствор из песка без будет дорого. Слово "песок" применяется к любому тонко измельченного материала, который не будет вредно влиять на цемент или известь и *, которая не подлежит распаду или распада. Песок почти единственный материал, который является достаточно дешевым, и которые могут выполнить эти требования. Смесь грубых и мелких зерен очень удовлетворительным, как это делает более плотным и сильным бетона с меньшим количеством цемента, чем когда только мелкозернистого песка является . используется следующие пески используются для строительных растворов:. пит или карьер, песок, речной песок и море песок Известь является оксид кальция. Он используется в больших количествах для раствора и штукатурки. Известь (негашеная) является белого твердого вещества, бурно реагирует с водой с образованием гидроксида кальция. Это делается путем нагревания известняка в особого рода печи называется "печи". Известь должна храниться в сухом месте, в противном случае он будет поглощать влагу. Лаймс могут быть разделены на три класса: 1. Богатые липы, которые содержат не более чем на 6 процентов примесей, утолить очень быстро, и полностью зависят от внешних * агентов для установки POWER4. Они широко используются для работ внутренних дел штукатурные. 2. Бедные липы, которые содержат от 15 до 30 процентов бесполезных примесей и обладают общими свойствами богатых липы, только в меньшей степени. 3. Гидравлические липы, которые содержат определенные пропорции примесей, которые при прокаливают, в сочетании с известью и наделяют его с ценным имуществом установления под водой или без внешних агентов. Известь является основным строительным материалом широко используется во всем мире, но это не было до поздних лет 19-го века, что больше оценка проблем сжигания топлива, участвующих стала очевидной. До этого времени требование для извести не была в значительной степени сельскохозяйственной и было произведено фермерами или небольших строителей, которые использовали его для приготовления строительных растворов и штукатурки. В промышленных требования увеличились были разработаны "работает" печи. Они были выложены огнеупорным кирпичом и взимается на регулярной основе с камнем и топлива. В мире существует много различных типов печей и вариаций в извести сжигания практике.