Materials Science and Technology is

Materials Science and Technology is the study of materials and how they can be fabricated to meet the needs of modern technology. Using the laboratory techniques and knowledge of physics, chemistry, and metallurgy, scientists are finding new ways of using metals, plastics and other materials.

Engineers must know how materials respond to external forces, such as tension, compression, torsion, bending, and shear. All materials respond to these forces by elastic deformation. That is, the materials return their original size and form when the external force disappears. The materials may also have permanent deformation or they may fracture. The results of external forces are creep and fatigue.

Compression is a pressure causing a decrease in volume. When a material is subjected to a bending, shearing, or torsion (twisting) force, both tensile and compressive forces are simultaneously at work. When a metal bar is bent, one side of it is stretched and subjected to a tensional force, and the other side is compressed.

Tension is a pulling force; for example, the force in a cable holding a weight. Under tension, a material usually stretches, returning to its original length if the force does not exceed the material's elastic limit. Under larger tensions, the material does not return completely to its original condition, and under greater forces the material ruptures.

Fatigue is the growth of cracks under stress. It occurs when a mechanical part is subjected to a repeated or cyclic stress, such as vibration. Even when the maximum stress never exceeds the elastic limit, failure of the material can occur even after a short time. No deformation is seen during fatigue, but small localized cracks develop and propagate through the material until the remaining cross-sectional area cannot support the maximum stress of the cyclic force. Knowledge of tensile stress, elastic limits, and the resistance of materials to creep and fatigue are of basic importance in engineering.

Creep is a slow, permanent deformation that results from a steady force acting on a material. Materials at high temperatures usually suffer from this deformation. The gradual loosening of bolts and the deformation of components of machines and engines are all the examples of creep. In many cases the slow deformation stops because deformation eliminates the force causing the creep. Creep extended over a long time finally leads to the rupture of the material.

Результаты (русский) 1:

Материаловедение и технология является изучение материалов и как они могут быть изготовлены для удовлетворения потребностей современной технологии. С помощью лабораторных методов и знания физики, химии и металлургии, ученые находят новые пути использования металлов, пластмассы и других материалов.Инженеры должны знать, как реагировать на материалы внешних сил, таких, как напряженность, сжатия, кручения, изгиб и сдвига. Все материалы отвечают на эти силы, упругой деформации. То есть материалы возвращаются их Оригинальный размер и форма когда внешние силы исчезает. Материалы также могут иметь остаточной деформации, или они могут перелом. Результаты внешних сил являются ползучести и усталость.Сжатие-это давление, вызывая снижение объема. Когда материал подвергается изгибу, стрижка, или кручения (скручивание) силы, растягивающие и сжимающие силы одновременно находятся на работе. Когда бар металла согнута, одна сторона его растягивается и подвергается растягивающих сил, и другой стороны сжимается.Напряженность является силой тяги; например силы в холдинг Вес кабеля. Под напряжение материал обычно растягивается, возвращаясь к своей первоначальной длины, если сила не превышает предел упругости материала. При большей напряженности материал не полностью вернуть в исходное состояние, и под большей силы материал разрывается.Fatigue is the growth of cracks under stress. It occurs when a mechanical part is subjected to a repeated or cyclic stress, such as vibration. Even when the maximum stress never exceeds the elastic limit, failure of the material can occur even after a short time. No deformation is seen during fatigue, but small localized cracks develop and propagate through the material until the remaining cross-sectional area cannot support the maximum stress of the cyclic force. Knowledge of tensile stress, elastic limits, and the resistance of materials to creep and fatigue are of basic importance in engineering.Creep is a slow, permanent deformation that results from a steady force acting on a material. Materials at high temperatures usually suffer from this deformation. The gradual loosening of bolts and the deformation of components of machines and engines are all the examples of creep. In many cases the slow deformation stops because deformation eliminates the force causing the creep. Creep extended over a long time finally leads to the rupture of the material.

Результаты (русский) 3:

науки и технологии материалов является изучение материалов и о том, как они могут быть сфабрикованы с целью удовлетворения потребностей современной технологии.используя лабораторные методы и знания по физике, химии, металлургии, ученые находят новые способы использования металла, пластика и других материалов.инженеры должны знать, как материалы, реагировать на внешние силы, такие как напряженности, сжатие, кручение, гибки и сдвиг.все материалы в ответ на эти силы упругая деформация.это материалы, возвращение их первоначального размера и формы, когда внешние силы, исчезает.материалы могут также иметь остаточной деформации или они, возможно, перелом.результаты внешних сил ползти и усталость.сжатие является давление приводит к снижению объема.когда материал, подвергается деформации, срывания или кручение (скручивание силу как растяжение и сжимающей силы одновременно на работе.когда металлическим прутом погнулась, с одной стороны, это тянется и подвергнут tensional силы, а с другой стороны, сжимается.это стягивает силы натяжения; например, силы в кабеле проведение вес.под напряжением, материал, обычно растягивается, вернувшись к своей первоначальной длине, если силы не должно превышать предел прочности материала.в соответствии с большей напряженности, материал не возвращает полностью в первоначальное состояние, и в соответствии с большей силы материал разрывы.усталость - это рост трещины под напряжением.это происходит, когда механическая часть подвергается повторным или циклические стресса, таких, как вибрация.даже когда максимальный стресс не превышает предел прочности, что материал может происходить даже после короткого времени.никакой деформации рассматривается на усталость, но небольшие локальные трещины разработки и пропаганды через материал до тех пор, пока остальные площадь поперечного сечения не может поддерживать максимальный стресс от циклических сил.знание растягивающее усилие, эластичные рамки, и сопротивление материалов, то и усталость, имеют определяющее значение в инженерном.гад - это медленный, остаточной деформации, что результаты постоянно действующими на материалы.материалы при высоких температурах, как правило, страдают от этого деформации.постепенное ослабление болты и деформация компонентов машин и двигатели все примеры подонка.во многих случаях медленно деформации останавливается, потому что деформации устраняет силы к подонка.урод затягивается на долгое время и, наконец, приводит к разрушению материала.